|Name:||Magnesium Alloy Block||DAMPING:||Absorbs Vibration For Longer Life, While Retaining Dimensional Stability.|
|STABILITY:||No Stress Relief After Machining; No Warps And Is Dent Resistant.||STRENGTH:||Excellent Strength And Stiffness Per Unit Weight.|
|Modulus Of Elasticity::||45 X 109Pa||Melting Range::||566 - 632°C|
|Thermal Conductivity::||76.9Wm-1k-1||Electrical Resistivity::||92nΩm|
AM60 Magnesium Alloy Block,
AZ91 Magnesium Alloy Block,
AZ61 Forged Magnesium Slab
AZ61 AZ80 AZ91 AM60 Magnesium Alloy Block Forged Magnesium Slab
Magnesium Alloy Block Introduction
Magnesium Alloy Block is mainly used in magnesium alloy production, aluminum alloy production,
steelmaking and desulfurization, aviation, and widely used in automobile manufacturing, light industry, metallurgical industry,chemical industry, electronic industry and instrument manufacturing industry.
We comply with the specifications:
GB5153-03, GB5154-04, AMS4377G, ASTM B90/B90M-15, MIL-DTL 32333, MIL-T-38749, QQ-M-44B, ASTM B107/B107M-13 and ASTM B91-97
Material grades: AZ31B, AZ61A, AZ80A, AZ91D, AZ41M, ZK60, AM50, AM60, ZM21, MIA, ME20M, EQ21, WE43, WE54, ZE41, etc.
Our main products and capabilities are as follows:
1. Magnesium tooling plate: Max. Thickness: 300mm; Max. Width: 2000mm; Max. Length: 6000mm
2. Magnesium alloy cast slab: Max. Size: 400 x 1000 x 3000mm
3. Magnesium alloy sheet: Min. Thickness: 0.5mm; Max. Width: 600mm; Max. Length: 2000mm
4. Magnesium cast billet: Min. Diameter 90mm; Max. Diameter: 600mm; Max. Length: 6000mm
5. Magnesium alloy extruded wire: Dia.1.0mm – 8.0mm in spool.
6. Magnesium alloy extruded rod: Min. Dia. 8mm; Max. Diameter: 450mm; Max. Length: 3000mm
7. Magnesium extrusions:
Round tube: Max. OD600mmx thickness 125mm
Square tube: 430 x 430mm
Flat bar: 920 x 160mm
U-Shape: 800 x 300mm
Rectangular: 700 x 200mm
8. Magnesium-Lithium Alloy rod, sheet, plate and tube.
AZ31B is a wrought magnesium base alloy with good room-temperature strength and ductility combined with corrosion resistance and weldability. Increased strength is obtained by strain hardening with a subsequent partial anneal (H24 and H26 tempers). Our sheet and plate’s size range is:
Sheet: thickness from 0.5mm to 6mm; Max. width is 600mm; Max. length is 6000mm;
Plate: thickness from 6 mm to 200mm; Max. width is 2000mm; Max. length is 6000mm;
Block: We can supply precut blocks according to customer’s requirements.
Sheet and plate in AZ31B find application in medium strength service at temperatures below 150°C. Diverse uses including aerospace, aircraft, concrete tools, 3C (cell phone / camera / computer), speaker cones and textile machinery can all benefit from light weight AZ31B.
AZ31B is non-magnetic and has high electrical and thermal conductivity filling the requirements for RFI and EMI shielding in the electronics and computer industries.
Superplastic forming of AZ31B sheet at elevated temperatures allows production of a wide variety of intricate parts for automotive uses. Monocoque construction utilizing formed sheet can be adapted to many commercial applications.
Mn: 0.20 – 1.0%
Coefficient of thermal expansion: 26.8 x 10-6K-1
Specific heat: 1040 Jkg-1k-1
Thermal conductivity: 76.9Wm-1k-1
Electrical resistivity: 92nΩm
Modulus of elasticity: 45 x 109Pa
Poissons ratio: 0.35
Melting range: 566 - 632°C
No thermal treatment is available for increasing the strength of this alloy after fabrication.
|Alloy and Temper||Thickness (mm)||
0.2% offset (MPa)
In 5.65 √A (%)
|AZ31B-O||0.5 – 1.5||125||221||10|
|1.5 – 6.3||105||221||9|
|6.3 - 75||105||221||8|
|AZ31B-H24||0.5 – 6.3||200||269||5|
|9.5 – 12.7||165||255||8|
|12.7 - 25||152||248||8|
|50 - 80||124||234||7|
|AZ31B-H26||6.3 - 10||186||269||6|
|10 – 12.5||179||262||6|
|12.5 - 20||172||255||5|
|20 – 25||159||255||5|
|25 - 40||152||241||5|
|40 - 50||148||241||5|
The sheet and plate shall conform to the tensile requirements in above Table unless other agreement is made between seller and purchaser. Mechanical Properties for sizes and tempers not shown in above Table shall be as agreed upon by seller and purchaser.
O temper: 67 Rockwell E
H24 temper: 83 Rockwell E
Excellent weldability with gas shielded arc using AZ61A (preferred) or AZ92A filler rod; post weld stress relief is required to prevent stress corrosion cracking. Resistance welding is excellent.
AZ31B, like all magnesium alloy sheet and plate, machines faster than any other metal. Providing the geometry of the part allows, the limiting factor is the power and speed of the machine rather than the quality of the tool material. The power required per cubic centimeter of metal removed varies from 9 to 14 watts per minute depending on machining operation.