Light Weight: | Absorbs Vibration For Longer Life, While Retaining Dimensional Stability. | Stablity: | No Stress Relief After Machining; No Warps And Is Dent Resistant. |
---|---|---|---|
COSTS: | Machine Dry, Without Oil Or Chemicals. | TOOLING: | 4 To 5 Times Greater Tool Life. |
FINISH: | Up To 5 Times More Machinable Than Rolled Aluminum. | NONMAGNETIC: | Good For Electrical And Computer Applications. |
WEIGHT: | Easier Handling Saves Energy And Time. | FLATNESS: | Eliminates Surface Machining. |
WELDING: | Strong Weldments Up To 95% Of Parent Metal, With Minimal Porosity. | ALKALI-RESISTANT: | Makes For Easy Cleaning. |
STRENGTH: | Excellent Strength And Stiffness Per Unit Weight. | NON-GALLING: | Sound And Rugged Surface, Offering A Low Coefficient Of Friction And Minimum Wear, |
High Light: | magnesium alloy engine block,magnesium drag blocks |
Fast machining Cast Homogenized AZ91 AZ91D Magnesium Alloy Block Plate Block 350x1100x3000mm Stable dimension
Xi'an Yuechen Metal Products. Co., Ltd. (XYMCO) - a manufacturer specialized in the magnesium tooling plate, Magnesium alloy plate, magnesium alloy slab, magnesium alloy sheet, magnesium alloy bar, magnesium alloy tube, magnesium alloy billet, magnesium alloy rod, magnesium alloy rod, magnesium alloy pipe, magnesium welding wire, magnesium alloy profile, magnesium alloy forging, magnesium alloy casting, magnesium alloy machining part.
We comply with the specifications: AMS 4377G, AMS 4382, ASTM B90/B90M and ASTM B107.
Material grades: AZ31B, AZ61A, AZ80A, ZK60, AM50, AM60, AZ91, EQ21, EZ33, EV31, WE43, WE54 and ZE41.
Our main products and capacities are as follows:
1. Magnesium tooling plate: Max. Thickness: 300mm; Max. Width: 3000mm; Max. Length: 6000mm
2. Magnesium alloy slab: Max. Size: 400 x 1000 x 2500mm
3. Magnesium alloy sheet: Min. Thickness: 0.5mm; Max. Width: 600mm; Max. Length: 2000mm
4. Magnesium cast bar: Min. Diameter 90mm; Max. Diameter: 600mm; Max. Length: 6000mm
5. Magnesium extrusions:
Round tube: Max. OD 600mmx thickness 125mm Square tube: 430 x 430mm Flat bar: 920 x 160mm
U-Shape: 800 x 300mm Rectangular: 700 x 200mm
6. Magnesium alloy machined part according to customer’s design
7. Magnesium anode as per customer’s design
Our products already were exported to USA, Japan, Israel, India, Germany, Iran, Columbia, Italy and UK. Good quality, good price and good delivery.
Looking forward to your enquiry and hope a prosperous cooperation can be established between us.
Mg content calculated as balance. AZ91A, B, C, D, and E have the same nominal composition but differ in ranges and/or specified impurity limits. This high purity alloy has excellent corrosion resistance. It is the most commonly used magnesium die casting alloy.
Component Value Min Max
Aluminum, Al 8.3 9.7
Copper, Cu 0.03
Iron, Fe 0.005
Magnesium, Mg 90
Manganese, Mn 0.13
Nickel, Ni 0.002
Silicon, Si 0.1
Zinc, Zn 0.35 1
Properties Value Min Max Comment
Physical
Density, g/cc 1.81 -- --
Mechanical
Hardness, Brinell 63 -- --
500 kg load, 10 mm
ball
Hardness, Knoop 84 -- --
Estimated from
Brinell
Hardness, Rockwell E 75 -- --
Hardness, Vickers 71 -- --
Estimated from
Brinell
Tensile Strength, Ultimate, MPa 230 -- --
Tensile Strength, Yield, MPa 150 -- -- at 0.2% Offset
Elongation at Break, % 3 -- -- in 50 mm
Modulus of Elasticity, GPa 44.8 -- -- In Tension
Compressive Yield Strength, MPa 165 -- -- at 0.2% offset
Poissons Ratio 0.35 -- --
Charpy Impact, J 2.7 -- -- V-notch
Fatigue Strength, MPa 97 -- --
R.R. Moore Test,
5E+8 Cycles
Shear Modulus, GPa 17 -- --
Shear Strength, MPa 140 -- --
Electrical
Electrical Resistivity, ohm-cm 1.43e-005 -- --
DAMPING | Absorbs vibration for longer life, while retaining dimensional stability. |
TOOLING | 4 to 5 times greater tool life. |
FINISH | Up to 5 times more machinable than rolled aluminum. |
COSTS | Machine dry, without oil or chemicals. |
WEIGHT | Easier handling saves energy and time. |
FLATNESS | Eliminates surface machining. |
STABILITY | No stress relief after machining; no warps and is dent resistant. |
WELDING | Strong weldments up to 95% of parent metal, with minimal porosity. |
ALKALI-RESISTANT | Makes for easy cleaning. |
CORROSION RESISTANT | A wide variety of chemical treatments exists for corrosion protection, alteration of surface appearance, and to provide a base for painting. Basic engineering precautions averts galvanic corrosion. |
STRENGTH | Excellent strength and stiffness per unit weight. |
NON-GALLING | Sound and rugged surface, offering a low coefficient of friction and minimum wear, |
REPID HEAT |
Ideal for a broad range of operating temperatures, from 350 degrees Fahrenheit to -30 degrees Fahrenheit. |
NONMAGNETIC | Good for electrical and computer applications. |
UNIT VOLUME |
Greater amount of finished magnesium material obtained, pound for pound. |
SALVAGE | Scrap retains a consistently high level of value. |
Contact Person: Mr. FRANK ZHANG
Tel: +86 189 66935266
Fax: 86-029-8263-6374